Interlayer for laminated glass, and laminated glass

ABSTRACT

An interlayer film for laminated glass includes a first layer containing a polyvinyl acetal resin and a plasticizer; and a second layer containing a polyvinyl acetal resin and a plasticizer, wherein the second layer is laminated on a first surface of the first layer, wherein a concentration of hydroxyl groups of the polyvinyl acetal resin in the first layer is different from a concentration of hydroxyl groups of the polyvinyl acetal resin in the second layer, and wherein at least one of the first layer, the second layer, or a portion of an interface between the first layer and the second layer contains a filler.

TECHNICAL FIELD

The present invention relates to an interlayer film for laminated glass used for obtaining laminated glass. Furthermore, the present invention relates to laminated glass including the interlayer film for laminated glass.

BACKGROUND ART

Laminated glass is excellently safe because it generates only a small amount of scattering glass fragments even when being broken by receiving an external shock. Therefore, laminated glass is widely used in automobiles, railroad cars, airplanes, ships, buildings, and the like. Laminated glass is manufactured by interposing an inter layer film for laminated glass between two glass places.

Interlayer films for laminated glass include a single-layered interlayer film having a structure consisting of a single layer and a multilayered interlayer film having a structure consisting of two or more layers.

The following Patent Literature 1 discloses, as an example of an interlayer film for laminated glass, a sound insulating layer containing 100 parts by weight of a polyvinyl acetal resin having a degree of socialization of 60 to 35 mol %, 0.001 to 1.0 part by weight of at least one kind of metal salt among alkali metal salts and alkaline earth metal salts, and a plasticizer in an amount of greater than 30 parts by weight. This sound insulating layer alone can be used as an interlayer film.

The following Patent Literature 1 also describes a multilayered interlayer film in which the aforementioned sound insulating layer and another layer are laminated. The other layer laminated on the sound insulating layer contains 100 parts by weight of a polyvinyl acetal resin having a degree of acetalization of 60 to 85 mol %, 0.001 to 1.0 part by weight of at least one kind of metal salt among alkali metal salts and alkaline earth metal salts, and a plasticizer in an amount of 30 parts by weight or less.

The following Patent Literature 2 discloses an interlayer film which is a polymer layer having a glass transition temperature of 33° C. or higher. Patent Literature 2 describes that the polymer layer is disposed between glass plates having a thickness of 4.0 mm or less.

The following Patent Literature 3 discloses an interlayer film containing (A) polyvinyl acetal, (B) at least one kind of plasticizer, (C) fumed silica, and (D) at least one kind of basic compound. In this interlayer film, a difference in refractive index between (C) fumed silica and plasticized polyvinyl acetal (A+B) is 0.015 or less, and a weight ratio of C/(A+B) is 2.7/100 to 60/100.

CITATION LIST Patent Literature

[Patent Literature 1] JP-A-2007-070200

[Patent Literature 2] US 2013/0236711A1

[Patent Literature 3]WO 2008/122608A1

SUMMARY

In a multilayered interlayer film of the related art as described in Patent Literature 1 to 3, the adhesion between respective layers is weak in some cases. Particularly, in a case where a content ratio of hydroxyl groups of a polyvinyl acetal resin contained in each of two adjacent layers varies, the adhesion between respective layers easily becomes weak.

One or more embodiments of the present inversion provide an interlayer film for laminated glass that can improve the adhesion between respective layers. One or more embodiments of the present invention provide laminated glass including the interlayer film for laminated glass.

According to one or more embodiments of the present invention, there is provided an interlayer film for laminated glass that includes a first layer containing a polyvinyl acetal resin and a plasticizer and a second layer containing a polyvinyl acetal resin and a plasticizer, in which the second layer is laminated on a first surface of the first layer, a content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer is different from a content ratio of hydroxyl groups of the polyvinyl acetal resin in the second layer, and the first layer or the second layer contains a filler or the interlayer film contains a filler in a portion of an interface between the first layer and the second layer.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the first layer or the second layer contains a filler.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the first layer contains a filler and the content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer is lower than the content ratio of hydroxyl groups of the polyvinyl acetal resin of the second layer.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, an absolute value of a difference between the content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer and the content ratio of hydroxyl groups of the polyvinyl acetal resin in the second layer is 5 mol % or greater.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, a content of the plasticizer in the first layer with respect to 100 parts by weight of the polyvinyl acetal resin in the first layer is greater than a content of the plasticizer in the second layer with respect to 100 parts by weight of the polyvinyl acetal resin in the second layer.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the filler has a hydroxyl group on a surface thereof.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the tiller is silica particles.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the content of the plasticizer in the first layer is 50 parts by weight or greater with respect to 100 parts by weight of the polyvinyl acetal ream in the first layer.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, in a case where the first layer contains a filler, a content of the filler in the first layer is 5 parts by weight to 64 parts by weight with respect to 100 parts by weight of the polyvinyl acetal resin in the first layer.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the interlayer film further includes a third layer containing a polyvinyl acetal resin and a plasticizer, and the third layer is laminated on a second surface side of the first layer that is opposite to the first surface.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, provided that a thickness of the interlayer film for laminated glass is T, a thickness of the first layer is 0.4T or less.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, when laminated glass is obtained by interposing the interlayer film for laminated glass between two sheets of green glass having a thickness of 2 mm based on JIS R3208, a visible light transmittance of the obtained laminated glass is 70% or greater.

In a certain aspect of the interlayer film for laminated glass according to one or more embodiments of the present invention, the interlayer film is used with a first glass plate with a thickness of equal to or less than 1 mm and arranged between the first glass plate and a second glass plate to be used for obtaining laminated glass.

According to one or more embodiments of the present inventions there is provided laminated glass including a first lamination glass member, a second lamination glass member, and the aforementioned interlayer film for laminated glass, in which the interlayer film for laminated glass is disposed between the first lamination glass member and the second lamination glass member.

In a certain aspect of the laminated glass according to one or more embodiments of the present invention, the first lamination glass member is a first glass plate, and a thickness of the first glass plate is 1 mm or less.

An interlayer film for laminated glass according to one or more embodiments of the present invention includes a first layer containing a polyvinyl acetal resin and a plasticizer and a second layer containing a polyvinyl acetal resin and a plasticizer, in which the second layer is laminated on a first surface of the first layer, a content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer is different from a content ratio of hydroxyl groups of the polyvinyl acetal resin in the second layer, and the first layer or the second layer contains a filler or the interlayer film contains a filler in a portion of an interface between the first layer and the second layer. Therefore, the interlayer film according to one or more embodiments of the present invention can improve the adhesion between respective layers.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a sectional view schematically showing an interlayer film for laminated glass according to one or more embodiments of the present invention.

FIG. 2 is a sectional view schematically showing an example of laminated glass including the interlayer film for laminated glass shown in FIG. 1.

DESCRIPTION OF EMBODIMENTS

Hereinafter, one or more embodiments of the present invention will be specifically described.

An interlayer film for laminated class (in the present specification, simply described as an “interlayer film” in some cases) according to one or more embodiments of the present invention has a structure consisting of two or more layers. The interlayer film according to one or more embodiments of the present invention may have a structure consisting of two layers or three or more layers. The interlayer film according to one or more embodiments of the present invention includes a first layer containing a polyvinyl acetal resin and a plasticizer. The interlayer film according to one or more embodiments of the present invention also includes a second layer containing a polyvinyl acetal resin and a plasticizer. In the interlayer film according to one or more embodiments of the present invention, the second layer is laminated on a first surface side of the first layer.

In the interlayer film according to one or more embodiments of the present invention, a content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer is different from a content ratio of hydroxyl groups of the polyvinyl acetal resin in the second layer.

In the interlayer film according to one or more embodiments of the present invention, the first layer or the second layer contains a filler. Alternatively, the interlayer film contains a filler in a portion of an interface between the first and the second layer. The first layer or the second layer may contain a filler, and the interlayer film may contain a filler in a portion of the interface between the first layer and the second layer.

Because of being constituted as above, the interlayer film according to one or more embodiments of the present invention can improve the adhesion between respective layers, and can inhibit the respective layers from being peeled off from each other.

From the viewpoint of uniformly and effectively improving the adhesion between respective layers, the first layer or the second layer may contain a filler. In a case where the interlayer film contains a filler in a portion of the interface between the first layer and the second layer, there are a portion in which the first layer and the second layer do not contact each other due to the filler and a portion in which the first layer and the second layer directly contact each other.

In a case where the first layer contains a filler, and the content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer is lower than the content ratio of hydroxyl groups of the polyvinyl acetal resin in the second layer, bending rigidity of laminated glass including the interlayer film can be improved. In order to obtain laminated glass, the interlayer film is disposed between a first glass plate and a second glass plate in many cases. Even though the first glass plate has a small thickness, in a case where the interlayer film according to one or more embodiments of the present invention is used, bending rigidity of the laminated glass can be sufficiently improved. Furthermore, even though both of the first and second glass plates have a small thickness, in a case where the interlayer film according to one or more embodiments of the present invention is used, bending rigidity of the laminated glass can be sufficiently improved. Herein, in a case where both of the first and second glass plates have a great thickness, bending rigidity of the laminated glass is further improved.

Furthermore, in a case where the first layer contains a filler, and the content ratio of hydroxyl groups of the polyvinyl acetal resin in the first layer is lower than the content ratio of hydroxyl groups of the polyvinyl acetal resin in the second layer, sound insulating properties of the laminated glass including the interlayer film can also be improved.

The aforementioned interlayer film may have a structure consisting or three or more layers, and may include a third layer in addition to the first and second layers. The interlayer film may further include the third layer containing a polyvinyl acetal resin and a plasticizer. In a case where the interlayer film includes the second and third layers, the third layer is disposed on a second surface side of the first layer that is opposite to the first surface described above. The third layer may contain a filler. Alternatively, the interlayer film may contain a filler in a portion of an interface between the first layer and the third layer.

A surface of the aforementioned second layer that is opposite to the aforementioned first layer side may be a surface on which a lamination glass member or a glass plate is laminated. A thickness of the glass plate laminated on the second layer may be 1 mm or less. The second surface of the first layer that is opposite to the first surface (surface on the second layer side) may be a surface on which a lamination glass member or a glass plate is laminated. A thickness of the glass plate laminated on the first layer may be 1 mm or less. A surface of the third layer that is opposite to the first layer side may be a surface on which a lamination glass member or a glass plate is laminated. A thickness of the glass plate laminated on the third layer may be 1 mm or less.

Due to the interlayer film, bending rigidity can be sufficiently improved. Therefore, the interlayer film is suitably used with a first glass plate with a thickness of equal to or less than 1 mm and a second glass plate with a thickness of equal to or less then 1 mm and arranged between the first glass plate and a second glass plate to be used for obtaining laminated glass. Furthermore, due to the interlayer film, bending rigidity can be sufficiently improved. Accordingly, the interlayer film is more suitably used with a first glass plate with a thickness of equal to or less than 1 mm and a second glass plate with a thickness of equal to or less than 1 mm and arranged between the first glass plate and a second glass plate to be used for obtaining laminated glass.

Hereinafter, one or more embodiments of the present invention will be described with reference to drawings.

FIG. 1 is a sectional view schematically showing an interlayer film for laminated class according to one or more embodiments of the present invention.

An interlayer film 11 shown in FIG. 1 is a multilayered interlayer film having a structure consisting or two or more layers. The interlayer film 11 is used for obtaining laminated glass. The interlayer film 11 is an interlayer film for laminated glass. The interlayer film 11 includes a first layer 1, a second layer 2, and a third layer 3. On a first surface 1 a of the first layer 1, the second layer 2 is disposed and laminated. On a second surface 1 b of the first layer 1 that is opposite to the first surface 1 a, the third layer 3 is disposed and laminated. The first layer 1 is an intermediate layer. Each of the second layer 2 and the third layer 3 is a protective layer, and in examples of the present embodiment, each of the second layer 2 and the third layer 3 is a surface layer. The first layer 1 is disposed and interposed between the second layer 2 and the third layer 3. Accordingly, the interlayer film 11 has multilayer structure (second layer 2/first layer 1/third layer 3) in which the second layer 2, the first layer 1, and the third layer 3 are laminated in this order.

Between the first layer 1 and the third layer 3, other layers stay be disposed. The first layer 1 and the third layer 3 may be directly laminated on each other. Examples of other layers include a layer containing polyethylene terephthalate and the like.

The first layer 1 contains a polyvinyl acetal resin and a plasticizer. The second layer 2 contains a polyvinyl acetal resin and a plasticizer. The third layer 3 may contain a polyvinyl acetal resin, and the third layer 3 may contain a plasticizer.

The interlayer film may include a first layer as a layer which is an intermediate layer in the interlayer film or a layer which is not a surface layer in the interlayer film. The interlayer film may include a second layer as a surface layer in the interlayer film. The interlayer files may include a third layer as a surface layer in the interlayer film.

hereinafter, the first layer, the second layer, and the third layer constituting the interlayer film according to one or more embodiments of the present invention and each of the components contained in the first layer, the second layer, and the third layer will be specifically described.

(Polyvinyl Acetal Resin or thermoplastic Resin)

The aforementioned first layer contains a polyvinyl acetal resin (hereinafter, described as a polyvinyl acetal resin (1) in some cases). The aforementioned second layer contains a polyvinyl acetal resin (2) hereinafter, described as a polyvinyl acetal resin (2) in some cases). The aforementioned third layer may contain a thermoplastic resin (hereinafter, described as a thermoplastic resin (3) in some cases), and may contain a polyvinyl acetal resin (hereinafter, described as a polyvinyl acetal resin (3) in some cases) as the thermoplastic resin (3). The polyvinyl acetal resin (1), the polyvinyl acetal resin (2), and the polyvinyl acetal resin (3) may be the same as or different from each other. Therefore, it is possible that the polyvinyl acetal resin (1) is different from the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3), because then sound insulating properties are further improved. One kind of each of the polyvinyl acetal resin (1), the polyvinyl acetal resin (2), and the polyvinyl acetal resin (3) may be used singly, or two or more kinds thereof may be used in combination. One kind of each of the thermoplastic resin (3) may be used singly, or two or more kinds thereof may be used in combination.

Examples of the thermoplastic resin include a polyvinyl acetal resin, an ethylene-vinyl acetate copolymer resin, an ethylene-acrylic acid copolymer resin, a polyurethane resin, a polyvinyl alcohol resin, and the like. Thermoplastic resins other than these may also be used.

The aforementioned polyvinyl acetal resin can be manufactured by, for example, acetalizing polyvinyl alcohol by using aldehyde. The polyvinyl acetal resin may be an acetalization product of polyvinyl alcohol. The polyvinyl alcohol is obtained by, for example, saponifying polyvinyl acetate. A degree of saponification of the polyvinyl alcohol is generally 70 to 99.9 mol %.

An average degree of polymerization of the aforementioned polyvinyl alcohol (PVA) may be 200 or greater, 500 or greater, 1,500 or greater, 1,600 or greater, 2,600 or greater, or 2,700 or greater. The average degree of polymerization of the polyvinyl alcohol may be 5,000 or less, 4,000 or less, or 3,500 or less. In a case where she average degree of polymerization is equal to or greater than the aforementioned lower limit, penetration resistance of laminated glass is further improved. In a case where the average degree or polymerization is equal to or less than the aforementioned upper limit, an interlayer film is easily formed.

The average degree of polymerization of the polyvinyl alcohol is determined by a method based on JIS K6726 “Testing methods for polyvinyl alcohol”.

The number of carbon atoms of an acetal group in the aforementioned polyvinyl acetal resin may be 3 to 5, for example 4 or 5.

As the aforementioned aldehyde, generally, aldehyde having 1 to 10 carbon atoms is suitably used. Examples of the aldehyde having 1 to 10 carbon atoms include formaldehyde, acetaldehyde, propionaldehyde, n-butyraldehyde, isobutyraldehyde, n-valeraldehyde, 2-ethylbutyraldehyde, n-hexylaldehyde, n-octylaldehyde, n-nonylaldehyde, n-decylaldehyde, benzaldehyde, and the like. Among these, acetaldehyde, propionaldehyde, n-butyraldehyde, isobutyraldehyde, n-hexylaldehyde, or n-valeraldehyde may be used, acetaldehyde, propionaldehyde, n-butyraldehyde, isobutyraldehyde, or n-valeraldehyde may be used, and n-butyraldehyde or n-valeraldehyde may be used. One Kind of the aldehyde may be used singly, or two or mere kinds thereof may be used in combination.

A content ratio of hydroxyl groups (amount of hydroxyl groups) of the polyvinyl acetal resin (1) may be 17 mol % or greater, 20 mol % or greater, or 22 mol % or greater. The content ratio or hydroxyl groups may be 30 mol % or less, less than 27 mol %, 25 mol % or less, or 24 mol % or less. In a case where the content ratio of hydroxyl groups is equal to or greater than the aforementioned lower limit, adhesion of the interlayer film is further improved. Particularly, in a case where the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) is 20 mol % or greater, reaction efficiency becomes high, and productivity becomes excellent. Furthermore, in a case where the content ratio of hydroxyl groups is less than 27 mol %, sound insulating properties of the laminated glass are further improved. Furthermore, in a case where the content ratio of hydroxyl groups is equal to or less than the aforementioned upper limit, flexibility of the interlayer film is improved, and handling of the interlayer film becomes easy.

The content ratio of hydroxyl groups (amount of hydroxyl groups) of the polyvinyl acetal resin (1) may be 17 mol % or greater, 20 mol % or greater, or 22 mol % or greater. The content ratio of hydroxyl groups may be 28 mol % or less, 27 mol % or less, 25 mol % or less, or 24 mol % or less. In a case where the content ratio of hydroxyl groups is equal to or greater than the aforementioned lower limit, mechanical strength of the interlayer film is further improved. Particularly, in a case where the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) is 20 mol % or greater, reaction efficiency becomes high, and productivity becomes excellent. In a case where the content ratio of hydroxyl groups is 28 mol % or less, sound insulating properties of the laminated glass are further improved. In a case where the content ratio of hydroxyl groups is equal to or leas than the aforementioned upper limit, flexibility of the interlayer film is improved, and handling of the interlayer film becomes easy. Particularly, although laminated glass including the interlayer film. In which the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) is 28 mol % or less, tends to have low bending rigidity, in a case where the filler is used, bending rigidity can be markedly improved.

A content ratio of hydroxyl groups of each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) may be 25 mol % or greater, 28 mol % or greater, 30 mol % or greater, 31.5 mol % or greater, 32 mol % or greater, or 33 mol % or greater. The content ratio of hydroxyl groups may be 38 mol % or less, 37 mol % or less, 36.5 mol % or less, or 36 mol % or less. In a case where the content ratio of hydroxyl groups is equal to or greater than the aforementioned lower limit, bending rigidity is further improved, and adhesion of the interlayer film is further improved. In a case where the content ratio of hydroxyl groups is equal to or less than the aforementioned upper limit, flexibility of the interlayer film is improved, and handling of the interlayer film becomes easy.

From the viewpoint of further improving sound insulating properties, the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) may be lower than the content ratio of hydroxyl groups of the polyvinyl acetal resin (2). In addition, from the viewpoint of further improving sound insulating properties, the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) may be lower than the content ratio of hydroxyl groups of the polyvinyl acetal resin (3). Moreover, from the viewpoint of further improving sound insulating properties, each of an absolute value of a difference between the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) and the content ratio of hydroxyl groups of the polyvinyl acetal resin (2) and an absolute value of a difference between the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) and the content ratio of hydroxyl groups of the polyvinyl acetal resin (3) may be 1 mol % or greater, 5 mol % or greater, 9 mol % or greater, 10 mol % or greater, or 12 mol % or greater. Each of the absolute value of the difference between the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) and the content ratio of hydroxyl groups of the polyvinyl acetal resin (2) and the absolute value of the difference between the content ratio of hydroxyl groups of the polyvinyl acetal resin (1) and the content ratio of hydroxyl groups of the polyvinyl acetal resin (3) may be 20 mol % or less. In a case where a filler such as silica particles is used, sound insulating properties tend to be further reduced due to the Influence of the filler, than in a case where the filler such as silica particles is not used. However, in a case where the relationship of the content ratio of hydroxyl groups described above is satisfied, sound insulating properties can be effectively improved.

The content ratio of hydroxyl groups of the polyvinyl acetal resin is a value obtained by expressing a molar fraction, which is determined by dividing an amount of ethylene group to which hydroxyl groups are bonded by a total amount of ethylene groups on a main chain, as a percentage. The amount of ethylene group to which hydroxyl groups are bonded can be measured based on, for example, JIS K6728 “Testing methods for polyvinyl butyral”.

A degree of acetylation (amount of acetyl groups) of the polyvinyl acetal resin (1) may be 0.01 mol % or greater, 0.1 mol % or greater, 7 mol % or greater, or 9 mol % or greater. The degree of acetylation of the polyvinyl acetal resin (1) may be 30 mol % or less, 25 mol % or less, 24 mol % or less, or 20 mol % or less. In a case where the degree of acetylation is equal to or greater than the aforementioned lower limit, compatibility between the polyvinyl acetal resin and a plasticizer is improved. In a case where the degree of acetylation is equal to or less than the aforementioned upper limit, moisture resistance of the interlayer film and the laminated glass is improved. Particularly, in a case where the degree of acetylation of the polyvinyl acetal resin (1) is 0.1 to 25 mol %, penetration resistance becomes excellent.

A degree of acetylation of each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) may be 0.01 mol % or greater, for example 0.5 mol % or greater. The degree of acetylation may be 10 mol % or less, for example 2 mol % or less. In a ease where the degree of acetylation is equal to or greater than the aforementioned lower limit, compatibility between the polyvinyl acetal resin and a plasticizer is improved. In a case where the degree of acetylation is equal to or less than the aforementioned upper limit, moisture resistance of the interlayer film and the laminated glass is improved.

The degree of acetylation is a value obtained by expressing a molar fraction, which is determined by dividing an amount of ethylene group to which acetyl groups are bonded by a total amount of ethylene groups on a main chain, as a percentage. The amount of ethylene groups to which acetyl groups are bonded can be treasured based on, for example, JIS K6728 “Testing methods for polyvinyl butyral”.

A degree of acetalization (in a case of polyvinyl butyral resin, a degree of butyralization) of the polyvinyl acetal resin (1) may be 47 mol % or greater, for example 60 mol % or greater. The degree of acetalization may be 85 mol % or less, 80 mol % or less, or 75 mol % or less. In a case where the degree of acetalization is equal to or greater than the aforementioned lower limit, compatibility between the polyvinyl acetal resin and a plasticizer is improved. In a case where the degree of acetalization is equal so or leas than the aforementioned upper limit, a reaction time necessary for manufacturing the polyvinyl acetal resin is shortened.

A degree of acetalization (in a case of polyvinyl butyral resin, a degree of butyralization) of each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) may be 55 mol % or greater, for example 60 mol % or greater. The degree of acetalization may be 75 mol % or less, for example 71 mol % or less. In a case where the degree of acetalization is equal to or greater than the aforementioned lower limit, compatibility between the polyvinyl acetal resin and a plasticizer is improved. In a case where the degree of acetalization is equal to or less than the aforementioned upper limit, a reaction time necessary for manufacturing the polyvinyl acetal resin is shortened.

The degree of acetalization is a value obtained by subtracting an amount of ethylene group, to which hydroxyl groups are bonded, and an amount of ethylene groups, to which acetyl groups are bonded, from a total amount of ethylene group on a main chain, dividing a value obtained as above by the total amount of ethylene groups on a main chain, and expressing a molar fraction obtained as above as a percentage.

The content ratio of hydroxyl groups (amount of hydroxyl groups), the degree of acetalization (degree of butyralization), and the degree of acetylation described above may be calculated from results measured by methods based on JIS K6728 “Testing methods for polyvinyl butyral”. Here, the measurement based on ASTM D1396-92 may be used. In a case where the polyvinyl acetal resin is a polyvinyl butyral resin, the content ratio of hydroxyl groups (amount of hydroxyl groups), the degree of acetalization (degree of butyralization), and the degree of acetylation can be calculated from results measured by methods based on JIS K6728 “Testing methods for polyvinyl butyral”.

From the viewpoint of further improving penetration resistance of the laminated glass, the polyvinyl acetal resin (1) may be a polyvinyl acetal resin (A) having a degree of acetylation (a) of less than 8 mol % and a degree of acetalization (a) of 65 mol % or greater or a polyvinyl acetal resin (B) having a degree of acetylation (b) of 8 mol % or greater. The polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) may be the polyvinyl acetal resin (A) or the polyvinyl acetal resin (B).

The degree or acetylation (a) of the polyvinyl acetal resin (A) may toe less than 8 mol %, 7.9 mol % or less, 7.8 mol % or less, 6.5 mol % or less, or 6 mol % or less. The degree of acetylation (a) may be 0.1 mol % or greater, 0.5 mol % or greater, 2 mol % or greater, 5 mol % or greater, or 5.5 mol % or greater. In a case where the degree of acetylation (a) is 0.1 mol % or greater and less than 8 mol %, migration of a plasticizer can be easily controlled, and sound insulating properties of the laminated glass are further improved.

The degree of acetalization (a) of the polyvinyl acetal resin (A) may be 65 mol % or greater, 66 mol % or greater, 67 mol % or greater, 67.5 mol % or greater, or 75 mol % or greater. The degree of acetalization (a) may be 85 mol % or less, 84 mol % or less, 83 mol % or less, or 82 mol % or less. In a case where the degree of acetalization (a) as equal to or greater than the aforementioned lower limit, sound insulating properties of the laminated glass are further improved. In a case where the degree of acetalization (a) is equal to or less than the aforementioned upper limit, a reaction time necessary for manufacturing the polyvinyl acetal resin (A) can be shortened.

A content ratio (a) of a hydroxyl group of the polyvinyl acetal resin (A) may be 18 mol % or greater, 19 mol % or greater, 20 mol % or greater, 21 mol % or greater, or 23 mol % or greater. The content ratio (a) of the hydroxyl group stay be 31 mol % or less, 30 mol % or less, 29 mol % or less, or 28 mol % or less. In a case where the content ratio (a) of the hydroxyl group is equal to or greater than the aforementioned lower limit, adhesion of the aforementioned second layer is further improved. In a case where the content ratio (a) of the hydroxyl group is equal to or less than the aforementioned upper limit, sound insulating properties of the laminated glass are further improved.

A degree of acetylation (b) of the polyvinyl acetal resin (B) may be 8 mol % or greater, 9 mol % or greater, 9.5 mol % or greater, 10 mol % or greater, or 10.5 mol % or greater. The degree of acetylation (b) may be 30 mol % or less, 28 mol % or less, 26 mol % or less, or 24 mol % or less. In a case where the degree of acetylation (b) is equal to or greater than the aforementioned lower limit, sound insulating properties of the laminated glass are further improved. In a case where the degree of acetylation (b) is equal co or less than the aforementioned upper limit, a reaction time necessary for manufacturing the polyvinyl acetal resin (B) can be shortened.

A degree of acetalization (b) of the polyvinyl acetal resin (B) may be 50 mol % or greater, 53 mol % or greater, 55 mol % or greater, or 60 mol % or greater. The degree of acetalization (to may be 78 mol % or less, 75 mol % or less, 72 mol % or less, or 70 mol % or less. In a case where the decree of acetalization (b) is equal to or greater than the aforementioned lower limit, sound insulating properties of the laminated glass are further improved. In a case where the degree of acetalization (b) is equal to or less than the aforementioned upper limit, a reaction time necessary or manufacturing the polyvinyl acetal resin (B) can be shortened.

A content ratio (b) of a hydroxyl group of the polyvinyl acetal resin (B) may be 18 mol % or greater, 19 mol % or greater, 20 mol % or greater, 21 mol % or greater, or 23 mol % or greater. The content ratio (b) of the hydroxyl group may be 31 mol % or less, 30 mol % or less, 20 mol % or less, or 28 mol % or less. In a case where the content ratio (b) of the hydroxyl group is equal to or greater than, the aforementioned lower limit, adhesion of the aforementioned second layer is further improved. In a case where the content ratio (b) or the hydroxyl group is equal to or less than the aforementioned upper limit, sound insulating properties of the laminated glass are further improved.

Each of the polyvinyl acetal resin (A) and the polyvinyl acetal resin (B) may be a polyvinyl butyral resin.

(Plasticizer)

The aforementioned first layer (including a single-layered interlayer film) contains a plasticizer (hereinafter, described as a plasticizer (1) in some cases). The aforementioned second layer contains a plasticizer (hereinafter, described as a plasticizer (2) in some cases). Furthermore, the aforementioned third layer may contain a plasticizer (hereinafter, described as a plasticizer (3) in some cases). The combination use of the polyvinyl acetal resin and the plasticizer appropriately improves the adhesion of the layer including the polyvinyl acetal resin and the plasticizer to a lamination glass member or other layers. The plasticizer is not particularly limited. The plasticizers (1), (2), and (3) may be the same as or different from each other. One kind of each of the plasticizers (1), (2), and (3) may be used singly, or two or more kinds thereof may be used in combination.

Examples of the aforementioned plasticizer include organic ester plasticizers such as a monobasic organic acid ester and a polybasic organic acid ester, organic phosphoric acid plasticizers such as an organic phosphoric acid plasticizer and an organic phosphorous acid plasticizer, and the like. Among these, organic ester plasticizers may be used. The aforementioned plasticizer may be a liquid plasticizer.

Examples of the aforementioned monobasic organic acid ester include a glycol ester obtained by reacting glycol with a monobasic organic acid, and the like. Examples of the glycol include triethylene glycol, tetraethylene glycol, tripropylene glycol, and the like. Examples of the monobasic organic acid include butyric acid, isobutyric acid, caproic acid, 2-ethyl butyrate, neptanoic acid, n-octylic acid, 2-ethylhexylic acid, n-nonylic acid, decylic acid, and the like.

Examples of the aforementioned polybasic organic acid ester include an ester compound of a polybasic organic acid and an alcohol having a linear or branched structure containing 4 to 8 carbon atoms, and the like. Examples or the polybasic organic acid include adipic acid, sebacic acid, azelaic acid, and the like.

Examples of the aforementioned organic ester plasticizers include triethylene glycol-di-2-ethyl propanoate, triethylene glycol-di-2-ethyl butyrate, triethylene glycol-di-2-ethyl hexanoate, triethylene glycol dicaprylate, triethylene glycol di-n-octanoate, triethylene glycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, dibutyl sebacate, dioctyl azelate, dibutyl carbitol adipate, ethylene glycol di-2-ethyl butyrate, 1,3-propylene glycol di-2-ethyl butyrate, 1,4-butylene glycol di-2-ethyl butyrate, diethylene glycol di-2-ethyl butyrate, diethylene glycol di-2-ethyl hexanoate, dipropylene glycol di-2-ethyl butyrate, triethylene glycol di-2-ethyl pentanoate, tetraethylene glycol di-2-ethyl butyrate, diethylene glycol dicapryiate, dihexyl adipate, dioctyl adipate, cyclohexyl hexyl adipate, a mixture of heptyl adipate and nonyl adipate, diisononyl adipate, diisodecyl adipate, heptyl nonyl adipate, dibutyl sebacate, oil-modified alkyd sebacate, a mixture of a phosphoric acid ester and an adipic acid ester, and the like. Organic eater plasticizers other than these may also be used, and so adipic acid ester other than the aforementioned adipic acid ester may also be used.

Examples of the aforementioned organic phosphoric acid plasticizers include tributoxyethyl phosphate, isodecylphenyl phosphate, triisopropyl phosphate, and the like.

The aforementioned plasticizer may be a diester plasticizer represented by the following Formula (1).

In Formula (1), each of R1 and R2 represents an organic group having 2 to 10 carbon atoms, R3 represents an ethylene group, an isopropylene group, or a n-propylene group, and p represents an integer of 3 to 10, Bach of R1 and R2 in Formula (1) may be an organic group having 5 to 10 carbon atoms or an organic group having 6 to 10 carbon atoms.

The aforementioned plasticizer may include di-(2-butoxyethyl)-adipate (DBEA), triethylene glycol di-2-ethylhexanoate (3GO), triethylene glycol di-2-ethylbutyrate (3GH), or triethylene glycol di-2-ethylpropanoate. It may include triethylene glycol di-2-ethylhexanoate (3GO), triethylene glycol di-2-ethylbutyrate (3GH), or triethylene glycol di-2-ethylpropanoate. It may include triethylene glycol di-2-ethylhexanoate or triethylene glycol di-2-ethylbutyrate. It may include triethylene glycol di-2-ethylhexanate.

Each of a content or the plasticizer (2) (hereinafter, described as a content (2) in some cases) with respect to 100 parts by weight of the polyvinyl acetal resin (2) and a content of the plasticizer (3) (hereinafter, described as a content (3) in some cases) with respect to 100 parts by weight or the thermoplastic resin (3) may be 10 parts by weight or greater, 15 parts by weight or greater, 20 parts by weight or greater, or 24 parts by weight or greater. Each of the content (2) and the content (3) may be 40 parts by weight or less, 35 parts by weight or less, 32 parts by weight or less, or 30 parts by weight or less. In a case where each of the content (2) and the content (3) is equal to or greater than the aforementioned lower limit, flexibility of the interlayer film is improved, and handling of the interlayer film becomes easy. In a case where each of the content (2) and she content (3) is equal to or less than the aforementioned upper limit, bending rigidity is further improved.

A content of the plasticizer (1) (hereinafter, described as a content (1) in some cases; with respect to 100 parts by weight of the polyvinyl acetal resin (1) may be 50 parts by weight or greater, 55 parts by weight or greater, or 60 parts by weight or greater. The content (1) may be 100 parts by weight or less, 90 parts by weight or less, 35 parts by weight or less, or 80 parts by weight or less. In a case where the content (1) is equal to or greater than the aforementioned lower limit, flexibility of the interlayer film is improved, and handling of the interlayer film becomes easy, in a case where the content (1) is equal to or less than the aforementioned upper limit, penetration resistance of the laminated glass is further improved.

In order to improve sound insulating properties of the laminated glass, the content (1) may be greater than the content (2) and the content (3). Particularly, although laminated glass including an interlayer film in which the content (1) is 55 parts by weight or greater tends to have low bending rigidity, in a case where a filler is used, bending rigidity can be markedly improved.

From the viewpoint of further improving sound insulating properties of the laminated glass, each of an absolute value of a difference between the content (2) and the content (1) and an absolute value of a difference between the content (3) and the content (1) may be 10 parts by weight or greater, 15 parts by weight or greater, or 20 parts by weight or greater. Each of the absolute value of the difference between the content (2) and the content (1) and the absolute value of the difference between the content (3) and the content (1) may be 80 parts by weight or less, 75 parts by weight or less, or 70 parts by weight or less.

(Filler)

The interlayer film contains a filler. The filler is present in the first layer, the second layer, or an interface between the first layer and the second layer. The use of the filler improves the adhesion between respective layers and improves bending rigidity without deteriorating sound insulating properties. One kind of the filler may be used singly, or two or more kinds thereof may be used in combination.

Examples of the filler include calcium carbonate particles, silica particles, and the like.

From the viewpoint of further improving the adhesion between respective layers, the filler may have a hydroxyl group on a surface thereof, furthermore, from the viewpoint of further improving the adhesion between respective layers, the filler may be silica particles.

A specific surface area of the silica particles determined by a BET method may be 50 m²/g or greater, 100 m²/g or greater, 200 m²/g or greater, 250 m²/g or greater, or 300 m²/g or greater. The specific surface area of the silica particles may be 500 m²/g or less. The specific surface area can be measured by a gas adsorption method by using a specific surface area/pore sire distribution analyzer. Examples of the analyzer include “ASAP 2420” manufactured by Shimadzu Corporation, and the like.

In the layer containing either the polyvinyl acetal resin or the thermoplastic resin and the filler, a content of the filler with respect to 100 parts by weight of the polyvinyl acetal resin or the thermoplastic resin may be 1 part by weight or greater, 5 parts by weight or greater, 10 parts by weight or greater, or 15 parts by weight or greater. The contest of the filler may be 70 parts by weight or less, 64 parts by weight or less, 60 parts by weight or less, 55 parts toy weight or less, 45 parts by weight or less, or 35 parts by weight or less. The content of the filler with respect to 100 parts by weight of the polyvinyl acetal resin (1) may be 1 part by weight or greater, 5 parts by weight or greater, 10 parts by weight or greater, or 15 parts by weight or greater. The content of the filler with respect to 100 parts by weight of the polyvinyl acetal resin (1) may be 70 parts by weight or less, 64 parts by weight or less, 60 parts by weight or less, 55 parts by weight or less, 45 parts by weight or less, or 35 parts by weight or less. The content of the silica particles may be equal to or greater than the aforementioned lower limit and equal to or less than the aforementioned upper limit. In a case where the content of the filler is equal to or greater than the aforementioned lower limit, the adhesion between respective layers is further improved, and bending rigidity is further improved. In a case where the content of the filler is equal to or less than the aforementioned upper limit, sound insulating properties are further improved.

(Heat Shielding Compound)

The aforementioned interlayer film may contain a heat shielding compound. Furthermore, each of the aforementioned first layer, second layer, and third layer may contain a heat shielding compound. One kind of the heat shielding compound may be used singly, or two or more kinds thereof may foe used in combination.

Component X:

The aforementioned interlayer film may contain, as a component X, at least one kind of compound among a phthalocyanine compound, a naphthalocyanine compound, and an anthracyanine compound. Each of the aforementioned first layer, second layer, and third layer may contain the component X. The component X is a heat shielding compound. One kind of the component X may be used singly, or two or more kinds thereof may be used in combination.

The component X is not particularly limited. As the component X, it is possible to use a phthalocyanine compound, a naphthalocyanine compound, and an anthracyanine compound known in the related art.

From the viewpoint of further improving heat shielding properties of the interlayer film and the laminated glass, the component X may be at least one kind of compound selected from the group consisting or phthalocyanine, a phthalocyanine derivative, naphthalocyanine, and a naphthalocyanine derivative, for example at least one kind of compound between phthalocyanine and a phthalocyanine derivative.

From the viewpoint of effectively improving heat shielding properties and maintaining a visible light transmittance at a much higher level over a long period of time, the component X may contain a vanadium atom or a copper atom. The component X may contain either a vanadium atom or a copper atom. The component X may be at least one kind of compound between phthalocyanine containing a vanadium atom or a copper atom and a phthalocyanine derivative containing a vanadium atom or a copper atom. From the viewpoint of further improving heat shielding properties of the interlayer film and the laminated glass, the component X may have a structural unit in which an oxygen atom is bonded to a vanadium atom.

A content of the component X in 100% by weight of the layer (the first layer, the second layer, or the third layer) containing the component X may be 0.001% by weight or greater, 0.005% by weight or greater, 0.01% by weight or greater, or 0.02% by weight or greater. The content of the component X may be 0.2% by weight or less, 0.1% by weight or less, 0.05% by weight or less, or 0.04% by weight or less. In a case where the content of the component X is equal to or greater than the aforementioned lower limit and equal to or less than the aforementioned upper limits heat shielding properties are sufficiently improved, and a visible light transmittance is sufficiently improved. For example, the visible light transmittance can become 70% or greater.

Heat Shielding Particles:

The aforementioned interlayer film may contain heat shielding particles. Each of the aforementioned first layer, second layer, and third layer may contain the heat shielding particles. The heat shielding particles are a heat shielding compound. The use of the heat shielding particles makes it possible to effectively block infrared rays (heat rays). One kind of the heat shielding particles may be used singly, or two or more kinds thereof may be used in combination.

from the viewpoint of further improving heat shielding properties of the laminated glass, the heat shielding particles may be metal oxide particles. The heat shielding particles may be particles formed of metal oxide (metal oxide particles.

Infrared rays having a wavelength of 780 nm or greater that is longer than a wavelength of visible light have a small energy amount compared to ultraviolet rays. However, infrared rays exert a strong thermal effect and are released as heat when being absorbed into a substance. Therefore, infrared rays are generally called heat rays. The use of the heat shielding particles makes it possible to effectively block infrared rays (heat rays). The heat shielding particles refer to particles that can absorb infrared rays.

Specific examples of the heat shielding particles include metal oxide particles such as aluminum-doped tin oxide particles, indium-doped tin oxide particles, antimony-doped tin oxide particles (ATO particles), gallium-doped zinc oxide particles (GZO particles), indium-doped zinc oxide particles (IZO particles), aluminum-doped zinc oxide particles (AZO particles), niobium-doped titanium oxide particles, sodium-doped tungsten oxide particles, cesium-doped tungsten oxide particles, thallium-doped tungsten oxide particles, rubidium-doped tungsten oxide particles, tin-doped indium oxide particles (ITO particles), tin-doped zinc oxide particles, and silicon-doped zinc oxide particles, lanthanum hexaboride (LaB₆) particles, and the like. Heat shielding particles other than these may also be used. Among these, metal oxide particles may be used because these particles have a high function of blocking heat rays. The metal oxide particles may be ATO particles, GZO particles, IZO particles, ITO particles, or tungsten oxide particles. They may be ITO particles or tungsten oxide particles. Especially, tin-doped indium oxide particles (ITO particles) may be used because these particles have a high function of blocking heat rays and are easily obtained, and tungsten oxide particles may also be used.

From the viewpoint of further improving heat shielding properties of the interlayer film and the laminated glass, the tungsten oxide particles may be metal-doped tungsten oxide particles. The “tungsten oxide particles” include metal-doped tungsten oxide particles. Specific examples of the metal-doped tungsten oxide particles include sodium-doped tungsten oxide particles, cesium-doped tungsten oxide particles, thallium-doped tungsten oxide particles, rubidium-doped tungsten oxide particles, and the like.

From the viewpoint of further improving heat shielding properties of the interlayer film and the laminated glass, cesium-doped tungsten oxide particles may be used. From the viewpoint of further improving heat shielding properties of the interlayer film and the laminated glass, the cesium-doped tungsten oxide particles may be tungsten oxide particles represented by Formula: Cs_(0.33)Wo₃.

An average particle size of the heat shielding particles may be 0.01 μm or greater, for example 0.02 μm or greater. The average particle sixe may be 0.1 μm or less, for example 0.05 μm or less. In a case where the average particle sire is equal to or greater than the aforementioned lower limit, shielding properties for heat rays are sufficiently improved. In a case where the average particle size is equal to or less than the aforementioned upper limit, dispersibility of the heat shielding particles is improved.

The aforementioned “average particle site” means a volume average particle size. The volume average particle site can be measured using a particle size distribution analyzer (“UPA-EX150” manufactured by NIKKISO CO., LTD.) or the like.

A content of the heat shielding particles in 100% by weight of the layer (the first layer, the second layer, or the third layer) containing the heat shielding particles may be 0.01% by weight or greater, 0.1% by weight or greater, 1% by weight or greater, or 1.5% by weight or greater. The content of the heat shielding particles may be 6% by weight or less, 5.5% by weight or less, 4% by weight or less, 3.5% by weight or less, or 3% by weight or less. In a case where the content of the heat shielding particles is equal to or greater than the aforementioned lower limit and equal to or less than the aforementioned upper limit, heat shielding properties are sufficiently improved, and a visible light transmittance is sufficiently improved.

(Metal Salt)

The aforementioned interlayer film may contain at least one kind of metal salt (hereinafter, described as a metal salt M in some cases) among alkali metal salts and alkaline earth metal salts. Each of the aforementioned first layer, second layer, and third layer may contain the metal, salt M. The use of the metal salt M makes it easy to control adhesiveness between the interlayer film and the lamination glass member or the adhesiveness between respective layers in the interlayer film. One kind of the metal salt M may be used singly, or two or more kinds thereof may be used in combination.

The metal salt M may contain at least one kind of metal selected from the group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, and Ba. The metal salt contained in the interlayer film may contain at least one kind of metal between K and Mg.

The metal salt M may be an alkali metal salt of an organic acid having 2 to 16 carbon atoms or an alkaline earth metal salt of an organic acid having 2 to 16 carbon atoms, for example a magnesium carboxylic acid salt having 2 to 16 carbon atoms or a potassium carboxylic acid salt having 2 to 16 carbon atoms.

The magnesium carboxylic acid salt having 2 to 16 carbon atoms and the potassium carboxylic acid salt having 2 to 16 carbon atoms are not particularly limited, and examples thereof include magnesium acetate, potassium acetate, magnesium propionate, potassium propionate, magnesium 2-ethylbutyrate, potassium 2-ethylbutanoate, magnesium 2-ethylhexanoate, potassium 2-ethylhexanoate, and the like.

A total content of Hg end K in the layer (the first layer, the second layer, or the third layer) containing the metal salt M may be 5 ppm or greater, 10 ppm or greater, or 20 ppm or greater. The total content of Mg and K may be 300 ppm or less, 250 ppm or less, or 200 ppm or less. In a case where the total content of Mg and K is equal to or greater than the aforementioned lower limit and equal to or less than the aforementioned upper limit, adhesiveness between the interlayer film and the lamination glass member or adhesiveness between the respective layers in the interlayer film can be controlled much better.

(UV Shielding Agent)

The aforementioned interlayer film may contain a UV shielding agent. Each of the aforementioned first layer, second layer, and third layer may contain a UV shielding agent. The use of the UV shielding agent more reliably prevents a visible light transmittance from decreasing even if the interlayer film and the laminated glass are used for a long period of time. One kind of the UV shielding agent may be used singly, or two or more kinds thereof may be used in combination.

The UV shielding agent includes a UV absorber. The UV shielding agent may be a UV absorber.

Examples of the UV shielding agent include a UV shielding agent containing a metal atom, a UV shielding agent containing a metal oxide, a UV shielding agent having a benzotriazole structure, a UV shielding agent having a benzophenone structure, a UV shielding agent having a triazine structure, a UV shielding agent having a malonic acid ester structure, a UV shielding agent having an oxalic acid anilide structure, a UV shielding agent having a benzoate structure, and the like.

Examples of the aforementioned UV absorber containing a metal atom include platinum particles, platinum particles whose surfaces are coated with silica, palladium particles, palladium particles whose surfaces are coated with silica, and the like. It is possible that the UV shielding agent is not heat shielding particles.

The aforementioned UV shielding agent, may be a UV shielding agent having a benzotriazole structure, a UV shielding agent having a benzophenone structure, a UV shielding agent having a triazine structure, or a UV shielding agent having a benzoate structure. It may be a UV shielding agent having a benzotriasole structure or a UV shielding agent having a benxophenone structure. It may be a UV absorber having a benrotriasole structure.

Examples of the aforementioned UV absorber containing a metal oxide include zinc oxide, titanium oxide, cerium oxide, and the like. The surface of the UV absorber containing a metal oxide may be coated. Examples of materials, with which the surface of the UV absorber containing a metal oxide is coated, include an insulative metal oxide, a hydrolysable organic silicon compound, a silicone compound, and the like.

Examples of the aforementioned UV absorber having a benzotriazole structure include UV absorbers having a benzotriazole structure, such as 2-(2′-hydroxy-5′-methylphenyl)benzotriazole (“Tinuvin P” manufactured by BASF SE), 2-(2′-hydroxy-3′,5′-di-t-butylphenyl)benzotriazole (“Tinuvin 320” manufactured by BASF SE), 2-(2′-hydroxy-3′-t-butyl-5-methylphenyl)-5-chlorobenzotriazole (“Tinuvin 326” manufactured by BASF SE), and 2-(2′-hydroxy-3′,5′-di-amylphenyl)benzotriazole (“Tinuvin 328” manufactured by BASF SE). The above UV shielding agent may be a UV absorber having a benzotriazole structure containing a halogen atom, for example a UV absorber having a benzotriazole structure containing a chlorine atom, because these have excellent UV absorbing performance.

Examples of she aforementioned UV absorber having a benzophenone structure include octabenzone (“Chimassorb 81” manufactured by BASF SE) and the like.

Examples of the aforementioned UV absorber having a triazine structure include “LA-F70” manufactured by ADEKA Corporation, 2-(4,6-diphenyl-1,3,5-triazin-2-yl)-5-[(hexyl)oxy]-phenol (“Tinuvin 1577FF” manufactured by BASF SE), and the like.

Examples of the UV shielding agent having a malonic acid ester structure include dimethyl 2-(p-methoxybenzylidene)malonate, tetraethyl-2,2-(1,4-phenylenedimethylidene)bismalonate, 2-(p-methoxybenzylidene)-bis(1,2,2,6,6-pentamethyl 4-piperidinyl)malonate, and the like.

Examples of commercially available products of the UV shielding agent having a malonic acid ester structure include Hostavin B-CAP, Hostavin PR-25, and Hostavin PR-31 (all manufactured by Clariant International Ltd.).

Examples of the aforementioned UV shielding agent having an oxalic acid anilide structure include oxalic acid diamides having a substituted aryl group on a nitrogen atom, such as N-(2-ethylphenyl)-N′-(2-ethoxy-5-t-butylphenyl)oxalic acid diamide, N-(2-ethylphenyl-N′-(2-ethoxy-phenyl)oxalic acid diamide, and 2-ethyl-2′-ethoxy-oxyanilide (“Sanduvor V50” manufactured by Clariant International Ltd.).

Examples of the aforementioned UV absorber having a benroate structure include 2,4-di-tert-butylphenyl-3,5-di-tert-butyl-4-hydroxybenzoate (“Tinuvin 120” manufactured by BASF SE) and the like.

From the viewpoint of further inhibiting a decrease in a visible light transmittance after a passage of time, a content of the UV shielding agent in 100% by weight of the layer (the first layer, the second layer, or the third layer) containing the UV shielding agent may be 0.1% by weight or greater, 0.2% by weight or greater, 0.3% by weight or greater, or 0.5% by weight or greater. The content of the UV shielding agent stay be 2.5% by weight or less, 2% by weight or less, 1% by weight or less, or 0.8% by weight or less. Particularly, in a case where the content of the UV shielding agent in 100% by weight of the layer containing the UV shielding agent is 0.2% by weight or greater, a decrease in a visible light transmittance of the interlayer film and the laminated glass that occurs after a passage of time can be markedly inhibited.

(Antioxidant)

The aforementioned interlayer film may contain an antioxidant. Each of the aforementioned first layer, second layer, and third layer may contain an antioxidant. One kind of the antioxidant may be used singly, or two or more kinds thereof may be used in combination.

Examples of the antioxidant include a phenol-based antioxidant, a sulfur-based antioxidant, a phosphorus-based antioxidant, and the like. The phenol-based antioxidant is an antioxidant having a phenol skeleton. The sulfur-based antioxidant is an antioxidant containing a sulfur atom. The phosphorus-based antioxidant is an antioxidant containing a phosphorus atom.

The antioxidant may be a phenol-based antioxidant or a phosphorus-based antioxidant.

Examples of the aforementioned phenol-based antioxidant include 2,6-di-t-butyl-p-cresol (BHT), butylated hydroxyanizole (BHA), 2,6-di-t-butyl-4-ethylphenol, stearyl-β-(3,5-di-t-butyl-4-hydroxyphenyl)propionate, 2,2′-methylenebis-(4-methyl-6-butylphenol), 2,2′-methylenebis- 4-ethyl-6-t-butylphenol), 4,4′-butylidene-bis-(3-methyl-6-t-butylphenol), 1,1,3-tris-(2-methyl-hydroxy-5-t-butylphenyl)butane, tetrakis[methylene-3-(3′,5′-butyl-4-hydroxyphenyl)propionate]methane, 1,3,3-tris-(2-methyl-4-hydroxy-5-t-butylphenol)butane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, bis(3,3′-t-butylphenol)butyric acid glycol ester, bis(3-t-butyl-4-hydroxy-5-methylbenzene propanoate)ethylenebis(oxyethylene), and the like. One kind or two or more kinds among these antioxidants are suitably used.

Examples of the aforementioned phosphorus-based antioxidant include tridecyl phosphite, tris(tridecyl) phosphite, triphenyl phosphite, trinonylphenyl phosphite, bis(tridecyl)pentaerythritol diphosphite, bis(decyl)pentaerythritol diphosphite, tris(2,4-di-t-butylphenyl)phosphite, bis(2,4-di-t-butyl-6-methylphenyl)ethyl ester phosphorous acid, tris(2,4-di-t-butylphenyl)phosphite, 2,2′-methylenebis(4,6-di-t-butyl-1-phenyloxy) (2-ethylhexyloxy)phosphorus, and the like. One kind or two or more kinds among these antioxidants are suitably used.

Examples of commercially available products of the above antioxidants include “IRGANOX 245” manufactured by BASF SE, “IRGAFOS 168” manufactured by BASF SE, “IRGAFOS 38” manufactured by BASF SE, “SUMILIZER BHT” manufactured by Sumitomo Chemical industry Company Limited, “IRGANOX 1010” manufactured by BASF SE, and the like.

In order to maintain a high visible light transmittance of the interlayer film and the laminated glass for a long period of time, a content of the aforementioned antioxidant in 100% by weight of the interlayer film or in 100% by weight of the layer (the first layer, the second layer, or the third layer) containing the antioxidant may be 0.1% by weight or greater. Furthermore, because the effects obtained by the addition of the antioxidant are saturated, the content of the antioxidant in 100% by weight of the interlayer film or in 100% by weight of the layer containing the antioxidant may be 2% by weight or loss.

(Other Components)

If necessary, each of she aforementioned first layer, second layer, and third layer may contain additives such as a coupling agent containing silicon, aluminum, or titanium, a dispersant, a surfactant, a flame retardant, an antistatic agent, a pigment, a dye, an adhesion adjuster, a moisture proof agent, a fluorescent whitening agent, and an infrared absorber. One kind of these additives may be used singly, or two or more kinds thereof may be used in combination.

(Other Details of Interlayer Film for Laminated Glass)

A thickness of the aforementioned interlayer film is not particularly limited. From the viewpoint of practically and from the viewpoint of sufficiently improving penetration resistance and bending rigidity of the laminated glass, the thickness of the interlayer film may be 0.1 mm or greater, for example 0.25 mm or greater. The thickness of the interlayer film may be 3 mm or less, for example 1.5 mm or less. In a case where the thickness of the interlayer film is equal to or greater than the aforementioned lower limit, penetration resistance and bending rigidity of the laminated glass are improved. In a case where the thickness of the interlayer film is equal to or less than the aforementioned upper limit, transparency of the interlayer film is further improved.

The thickness of the interlayer files is denoted by T. A thickness of the aforementioned first layer may be 0.0625 T or greater, for example 0.1 T or greater. The thickness of the first layer may be 0.4 T or less, 0.375 T or less, 0.25 T or less, or 0.15 T or less. In a case where the thickness of the first layer is 0.4 T or less, bending rigidity is further improved.

A thickness of each of the aforementioned second and third layers may be 0.3 T or greater, 0.3125 T or greater, or 0.375 T or greater. The thickness of each of the second and third layers may be 0.9375 T or less, for example 0.9 T or less. The thickness of each of the second and third layers may be 0.46875 T or less or 0.45 T or less. In a case where the thickness of each of the second and third layers is equal to or greater than the aforementioned lower limit and equal to or less than the aforementioned upper limit, rigidity and sound insulating properties of the laminated glass are further improved.

A total thickness of the aforementioned second and third layers may be 0.625 T or greater, 0.75 T or greater, or 0.85 T or greater. The total thickness of the second and third layers may be 0.9375 T or less, for example 0.9 T or less. In a case where the total thickness of the second and third layers is equal to or greater than the aforementioned lower limit and equal to or less than the aforementioned upper limit, rigidity and sound insulating properties of the laminated glass are further improved.

A method for manufacturing the interlayer film according to one or more embodiments of the present invention is not particularly limited. Examples of the method for manufacturing the interlayer film according to one or more embodiments of the present invention include a method of forming each layer by using each resin composition for forming each layer and then, for example, laminating the obtained each layer, a method of laminating each layer by co-extruding each resin composition for forming each layer by using an extruder, and the like. A manufacturing method using extrusion molding may be used because this method is suitable for continuous production.

The aforementioned second and third layers may contain the same polyvinyl acetal resin, and may contain the same polyvinyl acetal resin and the same plasticizer, because then manufacturing efficiency of the interlayer film becomes excellent. For the same reason, the second and third layers may be formed of the same resin composition.

According to one or more embodiments of the present invention, the aforementioned interlayer film has shapes of recesses and protrusions on at least one of the both surfaces thereof, and may have shapes of recesses and protrusions on both surfaces thereof. A method for forming the shapes of recesses and protrusions is not particularly limited, and examples thereof include a lip embossing method, an embossing roil method, a calendar roll method, a profile extrusion method, and the like. Among these, an embossing roll method may be used because this method makes it possible to form a large number of shapes of recesses and protrusions that are quantitatively constant recess and protrusion patterns.

(Laminated Glass)

FIG. 2 is a sectional view schematically showing an example of laminated glass including the interlayer film for laminated glass shown in FIG. 1.

Laminated glass 31 shown in FIG. 2 includes a first lamination glass member 21, a second lamination glass member 22, and the interlayer film 11. The interlayer film 11 is disposed and interposed between the first lamination glass member 21 and the second lamination glass member 22.

The first lamination glass member 21 is laminated on a first surface 11 a of the interlayer film 11. The second lamination glass member 22 is laminated on a second surface 11 b of the interlayer film 11 that is opposite to the first surface 11 a. The first lamination glass member 21 is laminated on a surface 2 a of the second layer 2 that faces outside. The second lamination glass member 22 is laminated on a surface 3 a of the third layer 3 that faces outside.

As described above, the laminated glass according to one or more embodiments of the present invention includes the first lamination glass member, the second lamination glass member, and the interlayer film, and the interlayer film is the interlayer film for laminated glass according to one or more embodiments of the present invention. In the laminated glass according to one or more embodiments of the present invention, the interlayer film is disposed between the first lamination glass member and the second lamination glass member.

Examples of the aforementioned lamination glass members include a glass plate, a polyethylene terephthalate (PET) film, and the like. The laminated glass includes not only laminated glass in which an interlayer film is interposed between two sheets of glass plates but also laminated glass in which an interlayer film is interposed between a glass plate and a PET film or the like. The laminated glass is a laminate including a glass plate, and at least one sheet of glass plate may be used in the laminated glass.

Examples of the glass plate include inorganic glass and organic glass. Examples of the inorganic glass include float plate glass, heat ray-absorbing plate glass, heat ray-reflecting plate glass, polished plate glass, figured glass, wired plate glass, and the like. The organic glass is synthetic resin glass as a substitute for inorganic glass. Examples of the organic glass include a polycarbonate plate, a poly(meth)acrylic resin plate, and the like. Examples of the poly(meth)acrylic resin plate include a polymethyl (meth)acrylate plate and the like.

A thickness of the aforementioned lamination glass member may be 1 mm or greater. The thickness of the lamination glass member may be 5 mm or less, for example 3 mm or less. In a case where the lamination glass member is a glass plate, a thickness of the glass plate may be 0.5 mm or greater, for example 0.7 mm or greater. The thickness of the glass place may be 5 mm or less, for example 3 mm or less. In a case where the lamination glass member is a PET film, a thickness of the PET film may be 0.03 mm to 0.5 mm.

The use of the interlayer film according to one or more embodiments of the present invention makes it possible to maintain bending rigidity of the laminated glass at a high level even if the laminated glass has a small thickness. From the viewpoint of lightening the laminated glass, reducing an environmental load by reducing the amount of materials of the laminated glass, or reducing an environmental load by improving fuel efficiency of an automobile by means of lightening the laminated glass, the thickness of the aforementioned glass plate may be 2 mm or less, 1.8 mm or less, 1.5 mm or less, 1 mm or less, 0.8 mm or less, or 0.7 mm or less.

A method for manufacturing the laminated glass is not particularly limited. For example, the interlayer film is interposed between the aforementioned first and second lamination glass members and aspirated under reduced pressure by being passed through pressing rolls or put into a rubber bag such that air remaining between the first lamination glass members the second lamination glass member, and the interlayer film is removed. Then, the first and second lamination glass members and the interlayer film are preliminarily bonded to each other at a temperature of about 70° C. to 110° C., thereby obtaining a laminate. Next, the laminate is put into an autoclave or pressed, and pressure-bonded at a temperature of about 120° C. to 150° C. under a pressure of 1 to 1.5 MPa. The laminated glass can be obtained in this way. At the time of manufacturing the laminated glass as above, the first layer, the second layer, and the third layer may be laminated.

The interlayer film and the laminated glass described above can be used in automobiles, railroad cars, airplanes, ships, buildings, and the like. Furthermore, the interlayer film and the laminated glass can also be used for other purposes. The interlayer film and the laminated glass may be an interlayer film and laminated glass for cars or buildings. They may be an interlayer film and laminated glass for cars. The interlayer film and the laminated glass can be used in front glass, side glass, rear glass, and roof glass of automobiles, and the like. The interlayer film and the laminated glass are suitably used in automobiles. The interlayer film is used for obtaining laminated glass for automobiles.

From the viewpoint of obtaining laminated glass having much better transparency, the aforementioned visible light transmittance of the laminated glass may be 60% or greater, for example 70% or greater. The visible light transmittance of the laminated glass can be measured based on JIS R3211 (1998). The visible light transmittance of the laminated glass, which is obtained by interposing the interlayer film for laminated glass according to one or sore embodiments of the present invention between two sheets of green glass (heat ray-absorbing plate glass) having a thickness of 2 mm based on JIS R3208, may be 70% or greater. The visible light transmittance may be 75% or greater.

Hereinafter, one or more embodiments of the present invention will be more specifically described based on examples, but the present invention is not limited to the examples.

The following materials were prepared.

(Polyvinyl acetal resin)

Polyvinyl acetal resins shown in the following tables 1 to 3 were appropriately used. For acetalization of all of the polyvinyl acetal resins used, n-butyraldehyde having 4 carbon atoms was used.

For the polyvinyl acetal resins, a degree of acetalization (degree of butyralization), a degree of acetylation, and a content ratio of hydroxyl groups were measured by the methods based on JIS K6728 “Testing methods for polyvinyl butyral”. Herein, in a case where the degree of acetalization, the degree of acetylation, and the content ratio of hydroxyl groups were measured according to ASTM D1396-92, the same results were obtained as in a case where the methods based on JIS K6728 “Testing methods for polyvinyl butyral” were used.

(Plasticizer)

Triethylene glycol di-2-ethylhexanoate (3GO)

Di-(2-butoxyethyl)-adipate (DBEA)

(Filler)

Filler (a) (silica particles, “AEROSIL 380” manufactured by NIPPON AEROSIL CO., LTD., specific surface area determined by a BET method: 380±30 m²/g)

Filler (b) (silica particles, “BZ-400” manufactured by Tosoh Silica Corporation, specific surface area determined by a BET method: 450 m²/g)

Filler (c) (silica particles, “AZ-204” manufactured by Tosoh Silica Corporation, specific surface area determined by a BET method: 300 m²/g)

filler (d) (silica particles, “AZ-201” manufactured by Tosoh Silica Corporation, specific surface area determined by a BET method; 300 m²/g)

(UV Shielding Agent)

Tinuvin 326 (2-(2′-hydroxy-3′-t-butyl-5-methylphenyl)-5-chlorobenzotriazole, “Tinuvin 326” manufactured by BASF SE)

(Antioxidant)

BHT (2,6-di-t-butyl-p-cresol)

Example 1

Preparation of composition for forming first layer:

100 parts by weight of a polyvinyl acetal resin of a kind shown in the following Table 1, 75 parts by weight of the plasticizer (3GO), 5 parts by weight of the filler (a), 0.2 parts by weight of the UV shielding agent (Tinuvin 326), and 0.2 parts by weight of the antioxidant (BHT) were mixed together, thereby obtaining a composition for forming a first layer.

Preparation of Composition for Forming Second Layer and Third Layer:

100 parts by weight of a polyvinyl acetal resin of a find shown in the following Table 1, 40 parts by weight of the plasticizer (3GO), 0.2 parts by weight of the UV shielding agent (Tinuvin 326), and 0.2 parts by weight of the antioxidant (BHT) were mixed together, thereby obtaining a composition for forming a second layer and a third layer.

Preparation of Interlayer Film:

The composition for forming the first layer and the composition or forming the second and third layers were co-extruded using a co-extruder, thereby preparing a second layer (thickness: 340 μm), a first layer (thickness: 100 μm), and a third layer (thickness: 340 μm) respectively.

Preparation of Laminated Film for Peeling Test:

For a peeling test, the first layer, the second layer, and the third layer each having a thickness of 760 μm were prepared using the composition for forming a first layer and the composition for forming second and third layers, and a laminate was prepared in which the second layer, the first layer, a PET film, and the third layer were laminated in this order at one end and the second layer, the first layer, and the third layer were laminated in this order at the other end. The laminate was held in a vacuum laminator for 30 minutes at 90° C. and pressed in a vacuum pressure, thereby obtaining a laminated film for a peeling test.

Preparation of Laminated Glass (for Measuring Visible Light Transmittance):

The obtained interlayer film was cut in a size of 30 cm (length)×30 cm (width). Then, two sheets of green glass (30 cm (length)×30 cm (width)×2 mm (thickness)) based on JIS R3208 were prepared. The obtained interlayer film was interposed between the two sheets of green glass, the resultant was held in a vacuum laminator for 30 minutes at 90° C., and pressed in a vacuum, thereby obtaining a laminate. In the laminate, the portion of the interlayer film sticking out of the glass plate was cut off, thereby obtaining laminated glass.

Examples 2 to 25 and Comparative Example 1

An interlayer film and laminated glass were obtained in the same manner as in Example 1, except that the type and the formulation amount of the polyvinyl acetal resin, the plasticizer, and the filler used in the composition for forming the first layer and the composition for forming the second and third layers were set as shown in the following Tables 1 to 3, and a thickness of each of the first layer, the second layer, and the third layer was set as shown in the following Tables 1 to 3. Furthermore, in Examples 2 to 25 and Comparative Example 1, the same type of UV shielding agent and antioxidant as in Example 1 were formulated in the same formulation amount (0.2 parts by weight with respect to 100 parts by weight of the polyvinyl acetal resin) as in Example 1.

(Evaluation)

(1) Visible Light Transmittance (A Light, Y Value, Initial A-Y (380 to 780 nm))

By using a spectrophotometer (“U-4100” manufactured by Hitachi High-Technologies Corporation.), a visible light transmittance of the obtained laminated glass at a wavelength of 330 to 780 nm was measured based on JIS R3211 (1998). The visible light transmittance was judged based on the following criteria.

[Criteria for Judging Visible Light Transmittance]

O: A visible light transmittance was 70% or greater.

X: A visible light transmittance was less than 70%.

(2) Maximum Load in Peeling Test

The obtained laminated film was cut in a size of 8 cm (length)×1 cm (width). At one end (2 cm (length)×1 cm (width)) of the cut laminated film, the second layer, the first layer, a PET film, and the third layer were laminated in this order, and at the other end (6 cm (length)×1 cm (width)) or the laminated film, the second layer, the first layer, and the third layer were laminated in this order. From the cut laminated film, the PET film was removed, and each of the third layer, the first layer, and the second layer was fixed to a tensilon jig manufactured by A&D Company, Limited and peeled off at a rate of 60 mm/min in a thermostatic chamber with a temperature of 25° C., thereby obtaining an elongation-load curve. Based on the obtained elongation-load curve, a maximum load observed until the film elongated up to 40 mm was evaluated. The greater the maximum load, the stronger the adhesion between respective layers.

Details and results of the above tests are shown in the following Tables 1 to 3. In the following Tables 1 to 3, formulated components other than the polyvinyl acetal resin, the plasticizer, and the filler are not described.

TABLE 1 Example Example Example Example Example Example Example Comparative 1 2 3 4 5 6 7 Example 1 Composition Thickness μm 100 100 100 100 100 100 100 100 of first Polyvinyl Average 3300 3300 3000 3000 3000 3000 3000 3000 layer acetal degree of resin polymerization of PVA Content ratio Mol % 23.3 23.3 23.3 23.3 23.3 23.3 23.3 23.3 of hydroxyl groups Degree of Mol % 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 acetylation Degree of Mol % 64.7 64.7 64.7 64.7 64.7 64.7 64.7 64.7 acetalization Content Part by 100 100 100 100 100 100 100 100 weight Plasticizer Type 300 300 300 300 300 300 300 300 Content Part by 75 75 75 75 75 75 75 75 weight Filler Type a a a a a — b — Content Part by 5 10 15 20 70 — 20 — weight Composition Thickness of each layer μm 340 340 340 340 340 340 340 340 of second Polyvinyl Average 1700 1700 1700 1700 1700 1700 1700 1700 and thrid acetal degree of layers resin polymerization of PVA Content ratio Mol % 30.1 30.1 30.1 30.1 30.1 30.1 30.1 30.1 of hydroxyl groups Degree of Mol % 0.8 0.8 0.8 0.8 0.8 0.8 0.8 0.8 acetylation Degree of Mol % 69.1 69.1 69.1 69.1 69.1 69.1 69.1 69.1 acetalization Content Part by 100 100 100 100 100 100 100 100 weight Plasticizer Type 300 300 300 300 300 300 300 300 Content Part by 40 40 40 40 40 40 40 40 weight Filler Type — — — — — a — — Content Part by — — — — — 20 — — weight Evaluation Visible light transmittance 0 0 0 0 0 0 0 0 Maximum load in peeling test [

] 9.1 10.1 13.1 14.7 17.9 14.4 13.5 8.5

indicates data missing or illegible when filed

TABLE 2 Example Example Example Example Example Example Example Example Example Example 8 9 10 11 12 13 14 15 16 17 Composition Thickness μm 100 100 100 100 100 100 100 100 100 100 of first Polyvinyl Average 3000 3000 3000 3000 3000 3000 3000 3000 2300 1700 layer acetal degree of resin polymerization of PVA Content ratio Mol % 23.3 23.3 23.3 23.3 23.3 23.3 23.3 23.3 23.3 23.3 of hydroxyl groups Degree of Mol % 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 acetylation Degree of Mol % 64.7 64.7 64.7 64.7 64.7 64.7 64.7 64.7 64.7 64.7 acetalization Content Part by 100 100 100 100 100 100 100 100 100 100 weight Plasticizer Type 300 300 300 300 300 300 300 300 300 300 Content Part by 75 75 75 75 75 75 75 75 75 75 weight Filler Type c c c c c c c d c c Content Part by 5 10 20 30 40 50 60 20 20 20 weight Composition Thickness of each layer μm 340 340 340 340 340 340 340 340 340 340 of second Polyvinyl Average 1700 1700 1700 1700 1700 1700 1700 1700 1700 1700 and thrid acetal degree of layers resin polymerization of PVA Content ratio Mol % 30.1 30.1 30.1 30.1 30.1 30.1 30.1 30.1 30.1 30.1 of hydroxyl groups Degree of Mol % 0.8 0.8 0.8 0.8 0.8 0.8 0.8 0.8 0.8 0.8 acetylation Degree of Mol % 69.1 69.1 69.1 69.1 69.1 69.1 69.1 69.1 69.1 69.1 acetalization Content Part by 100 100 100 100 100 100 100 100 100 100 weight Plasticizer Type 300 300 300 300 300 300 300 300 300 300 Content Part by 40 40 40 40 40 40 40 40 40 40 weight Filler Type — — — — — — — — — — Content Part by — — — — — — — — — — weight Evaluation Visible light transmittance 0 0 0 0 0 0 0 0 0 0 Maximum load in peeling test [

] 9.2 10.9 13.6 15.0 16.0 17.1 16.6 13.0 13.4 13.5

indicates data missing or illegible when filed

TABLE 3 Example Example Example Example Example Example Example Example 18 19 20 21 22 23 24 25 Composition Thickness μm 100 100 100 100 100 100 100 100 of first Polyvinyl Average 1700 2300 1700 2300 3000 3000 3000 1700 layer acetal degree of resin polymerization of PVA Content ratio Mol % 21.1 20.8 24.4 24.6 23.3 23.3 23.3 23.3 of hydroxyl groups Degree of Mol % 1.6 1.6 6.5 6.5 12.0 12.0 12.0 12 acetylation Degree of Mol % 77.3 77.6 69.1 68.9 64.7 64.7 64.7 64.7 acetalization Content Part by 100 100 100 100 100 100 100 100 weight Plasticizer Type 300 300 300 300 300 300 300 DBEA Content Part by 75 75 75 75 75 75 75 75 weight Filler Type c c c c — — — c Content Part by 20 20 20 20 — — — 20 weight Composition Thickness of each layer μm 340 340 340 340 340 340 340 340 of second Polyvinyl Average 1700 1700 1700 1700 1700 1700 1700 1700 and thrid acetal degree of layers resin polymerization of PVA Content ratio Mol % 30.1 30.1 30.1 30.1 30.1 30.1 30.1 30.1 of hydroxyl groups Degree of Mol % 0.8 0.8 0.8 0.8 0.8 0.8 0.8 0.8 acetylation Degree of Mol % 69.1 69.1 69.1 69.1 69.1 69.1 69.1 69.1 acetalization Content Part by 100 100 100 100 100 100 100 100 weight Plasticizer Type 300 300 300 300 300 300 300 DBEA Content Part by 40 40 40 40 40 40 40 40 weight Filler Type — — — — b c d — Content Part by — — — — 20 20 20 — weight Evaluation Visible light transmittance 0 0 0 0 0 0 0 0 Maximum load in peeling test [

] 12.5 12.1 13.7 13.5 14.3 13.9 14.0 13.1

indicates data missing or illegible when filed

The bending rigidity and sound insulating properties or laminated glass including the interlayer film of Examples 1 to 5 were better than those of laminated glass including the interlayer film of Example 6.

REFERENCE SIGNS LIST

-   1 . . . first layer -   1 a . . . first surface -   1 b . . . second surface -   2 . . . second layer -   2 a . . . surface facing outside -   3 . . . third layer -   3 a . . . surface facing outside -   11 . . . interlayer film -   11 a . . . first surface -   11 b . . . second surface -   21 . . . first lamination glass member -   22 . . . second lamination glass member -   31 . . . laminated glass

Although the disclosure has been described with respect to only a limited number of embodiments, those stilled in the art, having benefit of this disclosure, will appreciate that various other embodiments may be devised without departing from the scope of the present invention. Accordingly, the scope of the invention should be limited only by the attached claims. 

1. An interlayer film for laminated glass comprising: a first layer containing a polyvinyl acetal resin and a plasticizer; and a second layer containing a polyvinyl acetal resin and a plasticizer, wherein the second layer is laminated on a first surface of the first layer, wherein a concentration of hydroxyl groups of the polyvinyl acetal resin in the first layer is different from a concentration of hydroxyl groups of the polyvinyl acetal resin in the second layer, and wherein at least one of the first layer, the second layer, or a portion of an interface between the first layer and the second layer contains a filler.
 2. The interlayer film for laminated glass according to claim 1, wherein the first layer or the second layer contains the filler.
 3. The interlayer film for laminated glass according to claim 2, wherein the first layer contains the filler, and wherein the concentration of hydroxyl groups of the polyvinyl acetal resin in the first layer is lower than the concentration of hydroxyl groups of the polyvinyl acetal resin in the second layer.
 4. The interlayer film for laminated glass according to claim 3, wherein an absolute value of a difference between the concentration of hydroxyl groups of the polyvinyl acetal resin in the first layer and the concentration of hydroxyl groups of the polyvinyl acetal resin in the second layer is 5 mol % or greater.
 5. The interlayer film for laminated glass according to claim 1, wherein a content of the plasticizer in the first layer with respect to 100 parts by weight of the polyvinyl acetal resin in the first layer is greater than a content of the plasticizer in the second layer with respect to 100 parts by weight of the polyvinyl acetal resin in the second layer.
 6. The interlayer film for laminated glass according to claim 1, wherein the filler has a hydroxyl group on a surface thereof.
 7. The interlayer film for laminated glass according to claim 1, wherein the filler is silica particles.
 8. The interlayer film for laminated glass according to claim 1, wherein a content of the plasticizer in the first layer is 50 parts by weight or greater with respect to 100 parts by weight of the polyvinyl acetal resin in the first layer.
 9. The interlayer film for laminated glass according to claim 1, wherein the first layer contains the filler, and wherein a content of the filler in the first layer is 5 parts by weight to 64 parts by weight with respect to 100 parts by weight of the polyvinyl acetal resin in the first layer.
 10. The interlayer film for laminated glass according to claim 1, further comprising: a third layer containing a polyvinyl acetal resin and a plasticizer, wherein the third layer is laminated on a second surface side of the first layer that is opposite to the first surface.
 11. The interlayer film for laminated glass according to claim 1, wherein provided that a thickness of the interlayer film for laminated glass is T, a thickness of the first layer is 0.4 T or less.
 12. The interlayer film for laminated glass according to claim 1, wherein when laminated glass is obtained by interposing the interlayer film for laminated glass between two sheets of green glass having a thickness of 2 mm based on JIS R3208, a visible light transmittance of the obtained laminated glass is 70% or greater.
 13. The interlayer film for laminated glass according to claim 1, wherein the interlayer film is used with a first glass plate with a thickness of equal to or less than 1 mm and is arranged between the first glass plate and a second glass plate for obtaining laminated glass.
 14. Laminated glass comprising: a first lamination glass member; a second lamination glass member; and the interlayer film for laminated glass according to claim 1, wherein the interlayer film for laminated glass is disposed between the first lamination glass member and the second lamination glass member.
 15. The laminated glass according to claim 14, wherein the first lamination glass member is a first glass plate, and a thickness of the first glass plate is 1 mm or less. 